S1170G

特点

● 无铅兼容
不含卤素、锑、红磷等成分,废弃燃烧时不产生剧毒其他和残留有毒成分
高Tg无卤,Tg180℃(DMA)
UV Blocking/AOI兼容
低的Z轴热膨胀系数

应用领域

● xiaofeidianzi

● zhinengshouji

● qichedianzi

● diannao

● yiqiyibiao

  • 产品性能
  • 产品证书
  • 资料下载
Items Method Condition Unit Typical Value
Tg IPC-TM-650 2.4.24.4 DMA 180
Td IPC-TM-650 2.4.24.6 5% wt. loss 390
CTE (Z-axis) IPC-TM-650 2.4.24 Before Tg ppm/℃ 45
After Tg ppm/℃ 210
50-260℃ % 2.3
T260 IPC-TM-650 2.4.24.1 TMA min 60
T288 IPC-TM-650 2.4.24.1 TMA min 60
Thermal Stress IPC-TM-650 2.4.13.1 288℃, solder dip -- pass
Volume Resistivity IPC-TM-650 2.5.17.1 After moisture resistance MΩ.cm 5.65 x 107
E-24/125 MΩ.cm 2.71 x 107
Surface Resistivity IPC-TM-650 2.5.17.1 After moisture resistance 5.99 x 106
E-24/125 4.44 x 106
Arc Resistance IPC-TM-650 2.5.1 D-48/50+D-4/23 s 180
Dielectric Breakdown IPC-TM-650 2.5.6 D-48/50+D-4/23 kV 45+kV NB
Dissipation Constant (Dk) RC52%
IPC-TM-650 2.5.5.9 1GHz -- 4.4
Dissipation Factor (Df) RC52% IPC-TM-650 2.5.5.9 1GHz -- 0.010
Peel Strength (1Oz HTE copper foil) IPC-TM-650 2.4.8 A N/mm
After thermal Stress 288℃,10s N/mm 1.3
125℃ N/mm 1.1
Flexural Strength LW IPC-TM-650 2.4.4 A MPa 550
CW IPC-TM-650 2.4.4 A MPa 450
Water Absorption IPC-TM-650 2.6.2.1 E-1/105+D-24/23 % 0.12
Flammability UL94 C-48/23/50 Rating V-0
E-24/125 Rating V-0

Remarks:

1. specification sheet: ipc-4101/130, is for your reference only.

2. all the typical value is based on the 1.6mm specimen, while the tg is for specimen≥0.50mm.

3. All the typical values listed above are for your reference only and not intended for specification. Please contact Shengyi Technology Co., Ltd. for detailed information. All rights from this data sheet are reserved by Shengyi Technology Co., Ltd.

365投注平台 explanation: c=humidity conditioning, d=immersion conditioning in distilled water, e=temperature conditioning

365投注平台 the first digit following the letter indicates the duration of preconditioning in hours, the second digit the preconditioning temperature in ℃ and the third digit the relative humidity.